TPRC publication studies the effects of grit-blasting on titanium-thermoplastic composite joints
Researcher Vanessa Marinosci studies the correlation between mechanical performance and titanium surface morphology of co-consolidated Ti6Al4V-C/PEKK joints.
![Schematic representation of the co-consolidation process.](https://d2n4wb9orp1vta.cloudfront.net/cms/brand/CW/2021-CW/0621-cw-news-TPRC-publication-coconsolidation1.jpg;maxWidth=720)
Schematic representation of the co-consolidation process. Photo Credit: Vanessa M. Marinosci, Wouter J.B. Grouve, Matthjn B. de Rooij, Sebastiaan Whijskamp and Remko Akkerman.
ThermoPlastic composites Research Center (TPRC, Enschede, Netherlands) researcher Vanessa Marinosci has recently published an article called “Effect of grit-blasting on the fracture toughness of hybrid titanium-thermoplastic composite joints” in the International Journal of Adhesion and Adhesives. In the article, the correlation between mechanical performance and titanium surface morphology of co-consolidated Ti6Al4V-C/PEKK joints is described.
Various surface morphologies were obtained by grit-blasting the titanium surface using different blasting pressures. Subsequently, test coupons were manufactured by co-consolidating titanium-unidirectional C/PEKK in an autoclave. Topographical characterization of the titanium surface and evaluation of interfacial fracture toughness were carried out, in order to correlate joint mechanical performance to titanium's roughness parameters. Furthermore, crack surface analysis was conducted, by means of optical microscopy, to identify and quantify the failure mechanisms driving joint mechanical performance.
The research was conducted by TPRC in collaboration with the University of Twente (UT, Enschede, Netherlands). The financial support of the Dutch Research Council (NWO) and the TPRC members is gratefully acknowledged.
For more information on this topic, register for the next episode of the TPRC Talks “Joining with Thermoplastic Composites: Facing the Interface” on June 28, 2021 at 4:00 p.m. CET (10:00 a.m. EST).
Related Content
-
Sulapac introduces Sulapac Flow 1.7 to replace PLA, ABS and PP in FDM, FGF
Available as filament and granules for extrusion, new wood composite matches properties yet is compostable, eliminates microplastics and reduces carbon footprint.
-
Materials & Processes: Composites fibers and resins
Compared to legacy materials like steel, aluminum, iron and titanium, composites are still coming of age, and only just now are being better understood by design and manufacturing engineers. However, composites’ physical properties — combined with unbeatable light weight — make them undeniably attractive.
-
The making of carbon fiber
A look at the process by which precursor becomes carbon fiber through a careful (and mostly proprietary) manipulation of temperature and tension.